DS916 heat-conductive silicon
        Sourse:        Author:        Publish:2012-03-13        Hit:55

Products information    

DS916 heat-conductive silicon is one kind of organic silicon,which is neutral room temperature cured and have good adhesive and heat conduction performance at the same time.After being cured,the products could acquire excellent thermal tolerance and keep stable in the long-term utilization.Mostly they could be used to connect and fix the heater elements with radiators ,splice the high-power electric modules and radiators,which has replaced the traditional fixation.


Performance indicators




Before curing



Viscosity  (mPa·s)


Density( g/cm3)


Surface dry time


After curing

Tensile strength (MPa)


elongation at break(%)


Hardness(shore A)


Dielectric strength(kv/mm)


Volume resistance (Ω.cm)


Thermal conductivity (w/m·k)


Suitable temperature(℃)



*All properties are measured 7 days after curing at 25 ℃, 55% relative humidity conditions.


Operating processes and precautions

1. Must maintain the sizing surface clean and dry,remove dust and oil pollution which would affect the effect of bonding or sealing.According to the requirements ,choose suitable gluing thickness.

2. Moisture effect、temperature and humidity would affect curing rate when the glue solution was cured,hence,it is better to adjust the curing time as the circumstance is changing.

3. The remained glue solution should be sealed saved.If there are some condensates when use the glue solution again,you can use normally after removing them.

4. The products are non-dangerous goods,and keep a favorable ventilation working place.Avoid your eyes touching the uncured glue,if did,wash your eyes with clean water and go to a doctor immediately.



Boxes  50ml/b  200b/case

Boxes  100ml/b  100b/case

Boxes  300ml/b  25b/case


Storage and transport

  1. Under28℃ , dry conditions can be stored sealed for 9 months
  2. Transport and store as non-dangerous goods;